RECBAGS - sacs en film de Polyamide résistants au solvents et résistants à la chaleur
|
Material |
Modified Nylon (composite PA 6.6 + PA 6) |
|
Thickness |
60µ |
|
Elongation at yield |
MD 10% TD 11% |
|
Elongation at break 500mm/min |
MD 360% TD 520% |
|
Yield stress 500mm/min |
MD 20 MPA TD 18 MPA |
|
Flexural modulus |
2500 MPA |
|
Melting point (DSC) |
220° |
|
Deflection temperature at 66 psi |
178° |
|
Deflection temperature at 264 psi |
66° |
|
Density |
1.14 |
|
Continuous use temperature |
180° C |
|
Viscosity number |
4 |
|
Co-efficient of friction, static |
0.3~0.4 |
|
Co-efficient of friction, dynamic |
0.3~0.4 |
|
Oxygen permeability, 23° C / 0% RH |
40-42 cc/qm/day |
|
Water vapour 23° C / 85% RH |
120-130 cc/qm/day |
|
Transparency |
55% |
© OASE GmbH www.recbag.com
Les données ci-dessus sont des valeurs moyennes, différentes valeurs possibles.
Sous réserve de modifications et d'erreurs.